Welding wire SD-G3 0.8 mm 5kg

Description

AWS: A5.18 ER70S-6/ISO 14341-А G 42 4 М21

DSTU EN ISO 14341:2014

PURPOSE AND FIELD OF APPLICATION

Welding copper-coated wire SD-G3 is used for automatic and semi-automatic welding of carbon and low-alloy steels with yield strength of up to 420 N/mm2. The welding wire is widely used for welding pipelines, in ship-building, in automobile and machine building, as well as in construction. The wire is applied in operation with a thick-sheet metal. In this case the weld is formed for one pass (several passes).

APPLICATION CONDITIONS

Welding copper-coated wire is used for welding (surfacing) of products, parts and structures, made of carbon and low-alloy steels, in flat, vertical and overhead positions. It is possible to perform welding both in gas mixtures, and also in pure CO2. To produce the quality weld, the scale, rust and different oxide coatings should be removed. During the multi-pass welding the surface of the previous bead should be cleaned from a slag.

SPECIAL PROPERTIES

Due to the absence of non-metallic inclusions, the welding-technological properties of deposited material are improved after the plasma vacuum-arc treatment. The application of copper-plated welding wire SD-G3 allows increasing the quality of ready parts and products by forming a clean and reliable weld.

Welding wire SD-G3 guarantees:

– easy arc ignition due to optimal coating and perfect geometric parameters;
– minimum spattering during welding in CO2 and absence of spatters during welding in gas mixture М21;
– almost absence of a slag film on weld;
– high stability of arc burning.

Type: copper coated

CHEMICAL COMPOSITION OF DEPOSITED METAL, %

C

Si

Mn

P

S

Ni

Cr

Mo

V

Al

Ti+Zr

0,06-0,14

0,7-1,0

1,3-1,6

≤0,025

≤0,025 ≤0,15 ≤0,15 ≤0,15 ≤0,03 ≤0,02 ≤0,15

Total copper content is ≤ 0,35 %

MECHANICAL PROPERTIES OF WELD METAL

 Impact strength -400С  Tensile strength  Yield strength  Elongation
           ≥ 47 J    500-640 N/mm2    ≥ 420 N/mm2     ≥ 20%

WELDING CONDITIONS

 Diameter, mm

Current, А

Voltage, V

Feed rate, m/hour

Protective gas consumption, l/min

0,8

50-150

13-21

260-400

6-8

1,0

70-200

16-24

160-400

8-10

1,2

90-350

19-34

150-400

8-12

1,6

140-370

17-32

100-350

12-16

Welding should be performed at DC of reverse polarity.

Packaging:

1. Resistant cardboard box

2. Wire reeled on spool and packed hermetically in strong plastic bag

3. Silica gel bag inside box – for protection from air moisture impact

Metal spool

Plastic spool

BS 300

D 200

1; 1,2; 1,6 mm

0,8 mm

Weight -15kg.

Weight – 5 kg.

Certification 

 (EC Certificate of Conformity)

CE